供應進口SUS鎳合金光譜標樣光譜控樣。原裝德國進口。進口標準樣品質地均勻、精度高、認證等級高、塊狀標樣耐用等優(yōu)點已經越來越得到廣大中國用戶的青睞。*、 *、質量保證;常用控制標準樣品有現貨供應。
鎳基控樣 φ40mm X H 30mm
編號 類別
R Ni 10 高純鎳合金
R Ni 11 純鎳
R Ni 12 Ni Cu30
R Ni 13 Ni Cr15 Fe7 Mo15 W3
R Ni 14 Ni Cr20 Mo5 Co20 Ti1
R Ni 15 Ni Cr20 Fe20 Nb5 Ti1
Number | R Ni 10 | Number | R Ni 11 | Number | R Ni 12 | Number | R Ni 13 | Number | R Ni 14 | Number | R Ni 15 |
Type | Low Alloy | Type | Nickel | Type | Al/Cu | Type | Cr/Fe/Mo/W | Type | Co/Cr/Mo/Ti | Type | Cr/Fe/Mo/Nb |
Class | SUS | Class | SUS | Class | SUS | Class | SUS | Class | SUS | Class | SUS |
Comment | Batch 12 | Comment | Batch 23 | Comment | Batch 35 | Comment | Batch 33 | Comment | Batch 29 | Comment | Batch 40 |
Unit | Disc 40 mm Ø x 40 mm | Unit | Disc 40 mm Ø x 40 mm | Unit | Disc 40 mm Ø x 40 mm | Unit | Disc 40 mm Ø x 40 mm | Unit | Disc 40 mm Ø x 40 mm | Unit | Disc 40 mm Ø x 40 mm |
Al | <0.001 | Al | <0.01 | Al | 3.02 | Al | 0.21 | Al | 0.6 | Al | 0.5 |
C | <0.001 | C | 0.02 | C | 0.13 | B | <0.005 | B | 0.002 | B | 0.003 |
Co | <0.001 | Co | <0.01 | Co | 0.03 | C | <0.01 | C | 0.05 | C | 0.03 |
Cu | <0.01 | Cr | <0.01 | Cr | <0.01 | Co | 0.04 | Co | 19.44 | Co | 0.1 |
Fe | <0.02 | Fe | 0.07 | Cu | 29.61 | Cr | 15.9 | Cr | 20.93 | Cr | 18.4 |
Ni | >99.90 | Mg | 0.02 | Fe | 1.04 | Cu | 0.04 | Cu | 0.03 | Cu | 0.02 |
S | <0.005 | Mn | 0.26 | Mn | 0.56 | Fe | 5.5 | Fe | 0.3 | Fe | 18.9 |
Si | <0.001 | Ni | 99.5 | Ni | 65.2 | Mn | 0.08 | Mn | 0.41 | Mn | 0.09 |
P | <0.01 | P | <0.01 | Mo | 15.8 | Mo | 5.26 | Mo | 3.1 | ||
S | <0.01 | S | <0.01 | Nb | 0.04 | Nb | 0.05 | Nb | 5.1 | ||
Si | 0.12 | Si | 0.02 | Ni | 59.07 | Ni | 50.5 | Ni | 52.49 | ||
Ti | <0.01 | Ta | -0.04 | P | 0.002 | P | <0.01 | P | <0.01 | ||
Ti | 0.41 | S | <0.001 | S | <0.01 | S | <0.01 | ||||
Si | 0.07 | Si | 0.1 | Si | 0.07 | ||||||
Ta | <0.001 | Ti | 2.26 | Ta | <0.001 | ||||||
Ti | 0.03 | V | <0.01 | Ti | 0.9 | ||||||
V | 0.16 | W | 0.02 | V | 0.05 | ||||||
W | 3 | Zr | 0.02 | W | 0.04 | ||||||
Zr | <0.01 | Zr | 0.02 | ||||||||